| 标准： | astm b163， asme sb163 | 材料 | Alloy 200， UNS NO2200， 2.4066 |
|---|---|---|---|
| 产品名称 | 镍合金管 | 类型 | 无缝 |
| 表面： | 光亮表面 | 外径（圆形）： | 4 – 912 Mm |
| 厚度 | 1 – 30 Mm | 长度 | 1m-12m， Or As Required |
| 形状 | 圆形，"U "形 | 应用： | Construction Structure，Super Heater，Chemical Industry， Etc. |
| 强光 | Bright Surface Alloy， Offshore Engineering Nickel Alloy Tube， Alloy 200 Nickel Pipe | ||
ASME SB163 UNS NO2200， DIN 2.4066 Nickel Alloy Seamless Tube For Chemical Industry
Nickel Alloy 200， UNS N02200 / DIN 17751 2.4066 NA11 Ni 99，2 are solid solution strengthened， commercially pure wrought materials with good mechanical properties over a wide range of temperature and excellent 耐腐蚀性， in particular hydroxides. Nickel 201 was a modification of 200 to control carbon (.02 max) which keeps it from being embrittled by intergranular precipitate at temperature of 600° F to 1400° F. Typically， the elemental restrictions of both， Nickel Alloy 200 and nickel 201， dual-certified chemistry resulting in a single alloy with the desired characteristics of both alloys. 2.4066 Equal to Nickel Alloy 200.
Alloy 200 Standard:
DIN 17751 2.4066 DIN 17744 17750 17752 17753 2.4066
ASTM B161 B163 ASME SB161 SB163 N02200
BS 3072 3073 3074 3075 3076 NA11
Anticorrosion environment: Many kinds of organic solution/alkalinity liquids. Apply to the production soda water， the chlorine， the salty pedantry， the soap， Yuan wash the medicinal preparation， the food industry
ASTM B163 / ASME SB163 UNS N02200 is normally limited to service at temperatures below 600 °F. At higher temperature Nickel Alloy 200 products can suffer from graphitization which can result in severely compromised properties. When operating temperatures are expected to exceed 600° F， carbon content becomes critical. The lower carbon content of 镍 201 makes the material resistant to graphitization and therefore less subject to embrittlement. Nickel Alloy 200 & 201 are approved for construction of pressure vessels and components under ASME Boiler and 压力 Vessel Code Section VIII， Division 1. Nickel Alloy 200 is approved for service up to 600 °F while Nickel 201 is approved for service up to 1230 °F. Melting point is 2615-2635 °F.
ASTM B163 / ASME SB163 N02200 is unalloyed nickel with excellent corrosion resistance and excellent stability against alkaline media and good in a broad temperature range. Shows good under reducing conditions， e.g. hydrofluoric acid and . Shows good stability under oxidizing conditions (by creating a surface protection film). Material 2.4066 (Nickel Alloy 200) is used in the chemical industry and petrochemical industry.
What are the Characteristics of Alloy 200(UNS N02200)?
- 高度耐受各种还原性化学品
- 优异的耐苛性碱性能
- 高导电性
- 对蒸馏水和天然水具有出色的耐腐蚀性
- 耐中性和碱性盐溶液
- 优异的耐干氟性能
- 广泛用于处理烧碱
- Good thermal， electrical and magnetostrictive
- Offers some resistance to and at modest temperatures and concentrations
化学成分， %
| 倪 | 铁 | 铜 | C | 锰 | S | Si |
| 99.0 分钟 | 0.40 最大值 | 最大 0.25 | 0.15 最大值 | 0.35 最大值 | 0.01 最大值 | 0.35 最大值 |
规格
| 材料编号 | DIN 17744 17750 17751 17752 17753 2.4066 |
| EN 符号（短） | Ni 99.2 |
| AISI/SAE | - |
| UNS | ASTM B160 B161 B162 B163 B366 B564 B704 B705 B725 N02200 |
| AFNOR | - |
| 学士学位 | BS 3072 BS 3073 BS 3074 BS 3075 BS 3076 NA11 |
| 合金 | Nickel Alloy 200 |
| 注册作品'标签 | |
| 标准 | DIN 17744 17750 17751 17752 17753 2.4066 |
应用：
- 食品加工设备
- Marine and offshore engineering
- Salt production
- Caustic handling equipment
- Manufacture and handling of sodium hydroxide， particularly at temperatures above 300° F
- Reactors and vessels in which fluorine is generated and reacted with hydrocarbons