| 铍 | |
|---|---|
| 类别 | 金属有色金属Beryllium Alloy纯净元素 |
| 材料说明： | Beryllium is one of the lightest metals and has a high strength-to-weight ratio, stiffness-to-weight ratio, and very high specific heat, thermal conductivity, and heat of fusion. It has significant ductility, is readily machined and can be rolled, drawn, or extruded. It finds applications in nuclear reactors (neutron moderator and reflector), X-ray sources/detectors (X-ray transparency), IR target acquisition systems, inertial guidance instruments, computer parts, other aircraft and satellite structures, and heat sink constraining cores. Information provided by Materion Corporation (formerly Brush Wellman) and the references. Please note that there are health hazards associated with beryllium, especially when present as airborne particles generated during processing. As with any material, be aware of hazards and take steps to reduce exposure to a safe level. |
| 供应商 | 点击此处 查看该材料的所有可用供应商。 请 点击此处 如果您是供应商，并希望了解如何将您的清单添加到本资料中。 |
添加到文件夹： | |
打印版本
将数据导出到 CAD/FEA 程序| 物理特性 | 公制 | 英语 | 评论 | ||
|---|---|---|---|---|---|
| 密度 | 1.844 g/cc | 0.06662 磅/英寸 | |||
| 化学特性 | 公制 | 英语 | 评论 | ||
| 原子质量 | 9.012182 | 9.012182 | 1995 | ||
| 原子序数 | 4 | 4 | |||
| 热中子截面 | 0.0090 谷仓/原子 | 0.0090 谷仓/原子 | |||
| X 射线吸收边缘 | 110.68 Å | 110.68 Å | K | ||
| 电极电位 | -1.70 V | -1.70 V | |||
| 电负性 | 1.57 | 1.57 | 鲍林 | ||
| 离子半径 | 0.350 Å | 0.350 Å | 价态 +2 的晶体离子半径 | ||
| 0.440 Å | 0.440 Å | 晶体离子半径（价+1 | |||
| 机械性能 | 公制 | 英语 | 评论 | ||
| 硬度，洛氏硬度 B | 75 – 85 | 75 – 85 | |||
| 拉伸强度，极限 | 370 兆帕 | 53700 磅 | |||
| 拉伸强度，屈服 | 240 兆帕 | 34800 磅 | |||
| 断裂伸长率 | 3.0 % | 3.0 % | |||
| 弹性模量 | 303 GPa | 43900 ksi | |||
| 压缩屈服强度 | 270 兆帕 | 39200 磅 | Yield at 0.2% offset (10% higher than tensile yield strength). | ||
| 泊松比 | 0.070 – 0.18 | 0.070 – 0.18 | values between 0.07 and 0.18 have been reported for beryllium | ||
疲劳强度  | 160 兆帕 @# of Cycles 1.00e+7 | 23200 磅 @# of Cycles 1.00e+7 | Kt=3.07 and R = 0.1 | ||
| 240 兆帕 @# of Cycles 1.00e+7 | 34800 磅 @# of Cycles 1.00e+7 | smooth | |||
| 240 兆帕 @# of Cycles 10000 | 34800 磅 @# of Cycles 10000 | Kt=3.07 and R = 0.1 | |||
| 断裂韧性 | 10.6 – 12.3 MPa-m½ | 9.65 – 11.2 ksi-in½ | KIC for hot-pressed structural grades | ||
| 剪切模量 | 135 GPa | 19600 ksi | |||
| 剪切强度 | 345 兆帕 | 50000 磅 | hot-pressed block | ||
| 480 兆帕 | 69600 磅 | cross-rolled sheet | |||
| 夏比冲击 | 1.50 – 5.50 J | 1.11 – 4.06 英尺-磅 | Notch status unknown | ||
| 电气性能 | 公制 | 英语 | 评论 | ||
| 电阻率 | 0.00000430 欧姆-厘米 | 0.00000430 欧姆-厘米 | |||
| 磁感应强度 | -1.00e-6 | -1.00e-6 | cgs/g | ||
| 临界超导温度 | 0.0260 K | 0.0260 K | |||
| 热性能 | 公制 | 英语 | 评论 | ||
| 聚变热 | 1133 J/g | 487.4 BTU/lb | Be has an unusually high heat of fusion. | ||
| 蒸发热 | 24770 J/g | 10660 BTU/lb | |||
| 线性 CTE | 11.5 µm/m-°C @ 温度 25.0 °C | 6.39 µin/in-°F @ 温度 77.0 °F | increases rapidly until 100°C | ||
| 14.5 µm/m-°C 温度 25.0 - 300 °C | 8.06 µin/in-°F @ 温度 77.0 - 572 °F | ||||
| 16.5 µm/m-°C 温度 25.0 - 600 °C | 9.17 µin/in-°F 温度 77.0 - 1110 °F | ||||
| 18.4 µm/m-°C @Temperature 25.0 – 1000 °C | 10.2 µin/in-°F @Temperature 77.0 – 1830 °F | ||||
| 比热容 | 1.925 焦耳/克-摄氏度 | 0.4601 BTU/lb-°F | |||
| 导热性 | 216 W/m-K | 1500 BTU-in/hr-ft²-°F | |||
| 熔点 | 1273 – 1283 °C | 2323 – 2341 °F | |||
| 沸点 | 2471 °C | 4480 °F | |||
| 光学特性 | 公制 | 英语 | 评论 | ||
| 发射率 (0-1) | 0.61 | 0.61 | 650 纳米 | ||
| 反射系数，可见光（0-1） | 0.50 | 0.50 | 50% visible; 55% UV; 98% IR (10.6 µm) | ||
| 组件元素属性 | 公制 | 英语 | 评论 | ||
| 铍 | 100 % | 100 % | |||
| 描述特性 | |||||
| 化学文摘社编号 | 7440-41-7 | ||||
参考资料 本数据表。
以上显示的某些数值可能已从其原始单位进行了转换和/或四舍五入，以便
以一致的格式显示信息。需要更精确的科学或工程数据的用户
计算者可以点击属性值查看原始值以及转换为等效单位的原始值。
我们建议您在计算中只使用原始值或原始换算值，以尽量减少四舍五入。
错误。我们还请您参考 MatWeb 的 使用条款 关于这些信息。
以一致的格式显示信息。需要更精确的科学或工程数据的用户
计算者可以点击属性值查看原始值以及转换为等效单位的原始值。
我们建议您在计算中只使用原始值或原始换算值，以尽量减少四舍五入。
错误。我们还请您参考 MatWeb 的 使用条款 关于这些信息。
点击此处 查看
该数据表的所有属性值都是最初输入 MatWeb 时的值。