| T 400 系列不锈钢材料概览 | |
|---|---|
| 类别 | 金属黑色金属不锈钢T 400 Series Stainless Steel |
| 材料说明： | This property data is a summary of similar materials in the MatWeb database for the category “T 400 Series Stainless Steel”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods. |
| 供应商 | 未列出该材料的供应商。请 点击此处 如果您是供应商，并希望了解如何将您的清单添加到本资料中。 |
添加到文件夹： | |
打印版本
将数据导出到 CAD/FEA 程序| 物理特性 | 公制 | 英语 | 评论 |
|---|---|---|---|
| 密度 | 6.13 – 7.87 g/cc | 0.221 – 0.284 磅/英寸 | Average value: 7.72 g/cc Grade Count:309 |
| 颗粒大小 | 6.70 – 12.0 微米 | 6.70 – 12.0 微米 | Average value: 9.27 µm Grade Count:24 |
| 机械性能 | 公制 | 英语 | 评论 |
| 硬度，布氏硬度 | 131 – 594 | 131 – 594 | Average value: 254 Grade Count:106 |
| 硬度、努氏硬度 | 146 – 662 | 146 – 662 | Average value: 293 Grade Count:70 |
| 硬度，洛氏硬度 A | 51.1 – 56.4 | 51.1 – 56.4 | Average value: 53.0 Grade Count:6 |
| 硬度，洛氏硬度 B | 42.0 – 130 | 42.0 – 130 | Average value: 85.6 Grade Count:152 |
| 硬度，洛氏硬度 C | 10.0 – 59.0 | 10.0 – 59.0 | Average value: 40.5 Grade Count:106 |
| 硬度，维氏硬度 | 140 – 1100 | 140 – 1100 | Average value: 337 Grade Count:74 |
| 拉伸强度，极限 | 280 – 2070 兆帕 | 40600 – 300000 磅 | Average value: 861 MPa Grade Count:292 |
| 拉伸强度，屈服 | 165 – 1900 兆帕 | 23900 – 276000 磅 | Average value: 681 MPa Grade Count:261 |
| 断裂伸长率 | 1.00 – 46.0 % | 1.00 – 46.0 % | Average value: 19.6 % Grade Count:247 |
| 屈服伸长率 | 2.00 – 40.0 % | 2.00 – 40.0 % | Average value: 15.5 % Grade Count:7 |
| 减少面积 | 0.500 – 77.0 % | 0.500 – 77.0 % | Average value: 47.7 % Grade Count:58 |
| 弹性模量 | 199 – 215 GPa | 28900 – 31200 ksi | Average value: 200 GPa Grade Count:262 |
| Notched Tensile Strength | 793 – 2070 兆帕 | 115000 – 300000 磅 | Average value: 1740 MPa Grade Count:8 |
| 体积模量 | 166 GPa | 24100 ksi | Average value: 166 GPa Grade Count:4 |
| 泊松比 | 0.200 – 0.380 | 0.200 – 0.380 | Average value: 0.250 Grade Count:63 |
| 疲劳强度 | 85.0 – 772 兆帕 | 12300 – 112000 磅 | Average value: 389 MPa Grade Count:23 |
| 剪切模量 | 62.1 – 83.9 GPa | 9000 – 12200 ksi | Average value: 80.2 GPa Grade Count:64 |
| 伊佐德冲击 | 16.3 – 122 J | 12.0 – 90.0 英尺-磅 | Average value: 71.2 J Grade Count:28 |
| Izod Impact 无缺口 | 54.2 – 122 J | 40.0 – 90.0 英尺-磅 | Average value: 78.0 J Grade Count:3 |
| 夏比冲击 | 7.00 – 133 J | 5.16 – 98.1 英尺-磅 | Average value: 51.6 J Grade Count:32 |
| 电气性能 | 公制 | 英语 | 评论 |
| 电阻率 | 0.0000236 – 0.000120 欧姆-厘米 | 0.0000236 – 0.000120 欧姆-厘米 | Average value: 0.0000612 ohm-cm Grade Count:255 |
| 磁导率 | 400 – 2200 | 400 – 2200 | Average value: 885 Grade Count:51 |
| 热性能 | 公制 | 英语 | 评论 |
| 线性 CTE | 9.20 – 16.8 µm/m-°C | 5.11 – 9.33 µin/in-°F | Average value: 11.5 µm/m-°C Grade Count:247 |
| 比热容 | 0.427 – 0.477 焦耳/克-摄氏度 | 0.102 – 0.114 BTU/lb-°F | Average value: 0.461 J/g-°C Grade Count:197 |
| 导热性 | 15.0 – 27.0 W/m-K | 104 – 187 BTU-in/hr-ft²-°F | Average value: 24.0 W/m-K Grade Count:76 |
| 熔点 | 1370 – 1530 °C | 2500 – 2790 °F | Average value: 1480 °C Grade Count:195 |
| Solidus | 1370 – 1480 °C | 2500 – 2700 °F | Average value: 1450 °C Grade Count:188 |
| 液体 | 1480 – 1530 °C | 2700 – 2790 °F | Average value: 1510 °C Grade Count:188 |
| 最高使用温度，空气 | 620 – 1100 °C | 1150 – 2000 °F | Average value: 772 °C Grade Count:93 |
| 加工性能 | 公制 | 英语 | 评论 |
| 退火温度 | 593 – 999 °C | 1100 – 1830 °F | Average value: 796 °C Grade Count:3 |
| 热加工温度 | 750 – 1200 °C | 1380 – 2190 °F | Average value: 1010 °C Grade Count:3 |
| 组件元素属性 | 公制 | 英语 | 评论 |
| 铝 | 0.0100 – 4.00 % | 0.0100 – 4.00 % | Average value: 0.632 % Grade Count:20 |
| 碳，C | 0.00900 – 1.60 % | 0.00900 – 1.60 % | Average value: 0.212 % Grade Count:354 |
| 铬，Cr | 10.0 – 51.0 % | 10.0 – 51.0 % | Average value: 14.9 % Grade Count:355 |
| 铜，Cu | 0.500 – 2.50 % | 0.500 – 2.50 % | Average value: 1.56 % Grade Count:16 |
| 铁，Fe | 47.1 – 89.1 % | 47.1 – 89.1 % | Average value: 82.3 % Grade Count:355 |
| 锰，Mn | 0.0350 – 2.00 % | 0.0350 – 2.00 % | Average value: 0.969 % Grade Count:349 |
| 钼 | 0.0270 – 4.00 % | 0.0270 – 4.00 % | Average value: 0.788 % Grade Count:144 |
| 铌 + 钽 | 0.100 – 0.600 % | 0.100 – 0.600 % | Average value: 0.457 % Grade Count:23 |
| 镍 | 0.230 – 10.5 % | 0.230 – 10.5 % | Average value: 1.48 % Grade Count:149 |
| 铌（Cb） | 0.150 – 1.50 % | 0.150 – 1.50 % | Average value: 0.518 % Grade Count:25 |
| 氮，N | 0.0120 – 0.100 % | 0.0120 – 0.100 % | Average value: 0.0239 % Grade Count:26 |
| 磷，P | 0.0100 – 0.400 % | 0.0100 – 0.400 % | Average value: 0.0394 % Grade Count:299 |
| 钾 | 0.0600 % | 0.0600 % | Average value: 0.0600 % Grade Count:8 |
| 硒，Se | 0.150 % | 0.150 % | Average value: 0.150 % Grade Count:15 |
| 硅，Si | 0.0500 – 1.80 % | 0.0500 – 1.80 % | Average value: 0.903 % Grade Count:348 |
| 硫，S | 0.00100 – 4.00 % | 0.00100 – 4.00 % | Average value: 0.0472 % Grade Count:312 |
| 钽，Ta | 0.500 % | 0.500 % | Average value: 0.500 % Grade Count:5 |
| 钛 | 0.00500 – 1.40 % | 0.00500 – 1.40 % | Average value: 0.480 % Grade Count:38 |
| 钨，W | 0.750 – 3.00 % | 0.750 – 3.00 % | Average value: 1.30 % Grade Count:20 |
| 钒，V | 0.150 – 0.400 % | 0.150 – 0.400 % | Average value: 0.241 % Grade Count:20 |
以上显示的某些数值可能已从其原始单位进行了转换和/或四舍五入，以便
以一致的格式显示信息。需要更精确的科学或工程数据的用户
计算者可以点击属性值查看原始值以及转换为等效单位的原始值。
我们建议您在计算中只使用原始值或原始换算值，以尽量减少四舍五入。
错误。我们还请您参考 MatWeb 的 使用条款 关于这些信息。
以一致的格式显示信息。需要更精确的科学或工程数据的用户
计算者可以点击属性值查看原始值以及转换为等效单位的原始值。
我们建议您在计算中只使用原始值或原始换算值，以尽量减少四舍五入。
错误。我们还请您参考 MatWeb 的 使用条款 关于这些信息。
点击此处 查看
该数据表的所有属性值都是最初输入 MatWeb 时的值。