| Material Grade: | S32205 | Standard: | ASTM A790 |
|---|---|---|---|
| NDT: | ET， UT， HT ， PT | Size: | 1/2” To 18” |
| W.T.: | 0.3mm To 50mm | Length: | Single Random Length/ Double Random Length Or As Customer’s Actual Request |
| Packing: | Ply-wooden Case /Iron Case/ Bundle | Application: | Piping/ Heat Exchangers/Food Processing Equipment |
Duplex Stainless Steel Pipe ASTM A790 UNS S32205 Reactors Tanks
What is UNS S32205?
S32205 is a modern duplex stainless steel material combining austenitic and ferritic materials. It is known for its extremely high strength and resistance to stress corrosion cracking. These trademarks are approximately twice as strong as the austenitic and ferritic trademarks. It has better resistance and ductility than ferritic steels， but not up to the level of austenitic steels. Heat treatment is easy， but cold forming is difficult. Duplex (austenitic/ferritic) steel (Type 2205) containing 22% chromium has medium to high strength and superior resistance to general corrosion/stress， corrosion/cracking. It is generally used to make chemical processing equipment， pressure vessels and heat exchanger components. The alloy is resistant to chloride environments and chemical stress corrosion， and is approximately twice as strong as standard austenitic stainless steels. Requirements for higher mechanical strength / lighter weight， the alloy can be successfully used as a 300 series austenitic stainless steel replacement. s32205 easy to use many standard arc welding equipment for welding， but not recommended for oxyethylene block welding， due to the weld metal may present the phenomenon of carbonization. s32205 application planning application areas are: typical applications include oil and gas， chemical， electric power， and brewing industry. Widely used pumps， valves， flanges and piping systems. Martensitic stainless steel trademark is a group of corrosion-resistant and hardenable (using heat treatment) stainless steel alloys. Martensitic grades are pure chromium steels without nickel. They are magnetic， can be hardened by heat treatment， and are not as corrosion resistant as austenitic stainless steels. Martensitic grades are used primarily where hardness， strength and wear resistance are required.
Chemical Composition of ASTM A790 UNS S32205
| Element | Composition， % |
|---|---|
| TypeC | 2205 |
| Carbon | 0.030 max |
| Manganese | 2.00 max |
| Phosphorus | 0.030 max |
| Sulfur | 0.020 max |
| Silicon | 1.00 max |
| Nickel | 4.50 – 6.50 |
| Chromium | 22.00 – 23.0 |
| Molybdenum | 3.0 – 3.5 |
| Nitrogen | 0.14 – 0.20 |
Physical Properties of ASTM A790 UNS S32205
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Co-eff of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C ( J/kg.K) | Electrical Resistivity (nΩ.m) | |||
| 0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
| UNS S32205 / 2205 | 782 | 190 | 13.7 | 14.2 | – | 19 | – | 418 | 850 |
Mechanical Composition of ASTM A790 UNS S32205
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell C (HR C) | Brinell (HB) | ||||
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
ASTM A790 UNS S32205 Heat Treatment
| Process | Value |
|---|---|
| Annealing Temperature °F [°C] | 1870 – 2010 [1020 – 1100] |
| Quenching | Rapid Cooling in Air or Water |
Heat Resistance of ASTM A790 UNS S32205
The high oxidation resistance property of Grade 2205 is marred by its embrittlement above 300°C. This embrittlement can be modified by a full solution annealing treatment. This grade performs well at temperatures below 300°C.
Duplex Stainless Steel Pipe Application:
- Chemical Processing， Transport and Storage
- Oil and Gas Exploration and Offshore Rigs
- Marine Environments
- Architectural and structural engineering
- Medical equipment
- Papermaking equipment
- Sewage treatment equipment