| Standard: | ASTM A213 / ASME SA213 | Material Grade: | T22，T23 |
|---|---|---|---|
| Size: | According To Client’s Request | Length: | 6M/12M |
| Packing Details: | Ply-wooden Case /Iron Case/ Bundle With Plastic Cap | Certificate: | ISO9001-2008， API 5L， API 5CT |
| High Light: | Alloy Steel Boiler Tube， T22 Seamless Alloy Steel Tube， Heat Exchanger Alloy Steel | ||
ASTM SA213 T22 T23 Alloy Steel Seamless Tube For Boiler And Heat Exchanger
SA-213 T22 is a steel grade in the ASME SA-213M standard， which is 2.25Cr-1Mo chromium molybdenum high-temperature ferrite steel pipe for boilers and superheaters. In 1985， China transplanted it to GB5310 and named it 12Cr2MoG. The oxidation resistance temperature of T22 is slightly higher than that of 12Cr1MoVG， but its strength performance is slightly lower. This steel has good processing and welding properties， as well as good durability and plasticity. Therefore， it has been widely used in harsh working environments， such as various heating pipelines and high-pressure vessels in thermal power， nuclear power， and some hydrogen equipment.
T23 heat treatment system specified in ASME SA213 standard is: normalizing+tempering (normalizing temperature ≥ 1040 ℃， tempering temperature ≥ 730 ℃)， yield strength ≥ 400MPa， tensile strength ≥ 500MPa， elongation ≥ 20%， and hardness ≤ 220HB.
The allowable stress of T23 steel is twice that of T22 steel， and its 580 ℃ rupture strength is 1.4 times that of 12Cr1MoV steel. The rupture strength of T23 steel is equal to that of 12Cr21MoWVTiB (G102) steel， and it has high impact toughness and good moisture permeability. It is suitable for manufacturing superheaters， reheaters， and water-cooled walls of large power plant boilers.
ASTM A213/ASME SA213 T2， T11， T12， T22， T91， T92 Chemical Composition and Mechanical Properties
| Grade | Chemical Composition% | ||||||||
| C | Si | Mn | P， S Max | Cr | Mo | Ni Max | V | Al Max | |
| T2 | 0.10~0.20 | 0.10~0.30 | 0.30~0.61 | 0.025 | 0.50~0.81 | 0.44~0.65 | – | – | – |
| T11 | 0.05~0.15 | 0.50~1.00 | 0.30~0.60 | 0.025 | 1.00~1.50 | 0.44~0.65 | – | – | – |
| T12 | 0.05~0.15 | Max 0.5 | 0.30~0.61 | 0.025 | 0.80~1.25 | 0.44~0.65 | – | – | – |
| T22 | 0.05~0.15 | Max 0.5 | 0.30~0.60 | 0.025 | 1.90~2.60 | 0.87~1.13 | – | – | – |
| T91 | 0.07~0.14 | 0.20~0.50 | 0.30~0.60 | 0.02 | 8.0~9.5 | 0.85~1.05 | 0.4 | 0.18~0.25 | 0.015 |
| T92 | 0.07~0.13 | Max 0.5 | 0.30~0.60 | 0.02 | 8.5~9.5 | 0.30~0.60 | 0.4 | 0.15~0.25 | 0.015 |
| Grade | Chemical Composition% | Mechanical Properties | |||||||
| W | B | Nb | N | T. S | Y. P | Elongation | Hardness | ||
| T2 | – | – | – | – | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) | |
| T11 | – | – | – | – | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) | |
| T12 | – | – | – | – | ≥ 415MPa | ≥ 220MPa | ≥ 30% | 163HBW(85HRB) | |
| T22 | – | – | – | – | ≥ 415MPa | ≥ 205MPa | ≥ 30% | 163HBW(85HRB) | |
| T91 | – | – | 0.06~0.10 | 0.03~0.07 | ≥ 585MPa | ≥ 415MPa | ≥ 20% | 250HBW(25HRB) | |
| T92 | 1.50~2.00 | 0.001~0.006 | 0.04~0.09 | 0.03~0.07 | ≥ 620MPa | ≥ 440MPa | ≥ 20% | 250HBW(25HRB) | |
ASTM A213/ASME SA213 T2， T11， T12， T22， T91， T92 Tolerance
Permissible variations from the specified minimum wall thickness shall be in accordance with Specification A1016/A1016M.
| Outside Diameter | OD Tolerance | WT Tolerance | Ovality Tolerance | Cut Length Tolerance |
| OD≤ 12， 7 mm | ± 0， 13 mm | ± 15 % | – | + 3， 18 mm， – 0 mm |
| 12， 7 mm < OD ≤ 38， 1 mm | ± 0， 13 mm | ± 10 % | max， 1， 65 mm | + 3， 18 mm， – 0 mm |
| 38， 1 mm < OD ≤ 88， 9 mm | ± 0， 25 mm | ± 10 % | max， 2， 41 mm | + 4， 76 mm， – 0 mm |
Applications
- Petrochemical Industry
- Chemical Industry
- Nuclear Power Plant Industry
- Oil and Gas Industry
- Research & Development
- Mega Projects & Defense & Development Industries
- Pulp & Paper Indusry