| Product: | SMLS Tube | Standard: | ASTM B622 |
|---|---|---|---|
| Grade: | UNS NO6022 / C22 | Material: | Hastelloy Nickel Alloy |
| Testing: | ET， HT， Flattening Test; Expansion Test， Mercurous Nitrate Test; Ammonia Vapor Test; Chemical Analysis; Microscopical Examination; Tension Testing. | Package: | Ply-wooden Case |
| High Light: | UNS NO6022 Nickel Alloy Tube， Seamless Low Carbon Nickel Alloy Tube | ||
ASTM B622 UNS NO6022 Hastelloy C22 Low Carbon Nickel Alloy Seamless Tubes
TONG CHUANG Group as one of the leading suppliers in China to supply nickel alloy and tubes，etc.，we have many experiences in exporting.
ASTM B622 This specification covers and tube of nickel and nickel-cobalt alloys.
Alloy C22 is commonly referred to by the tradename Hastelloy C22 and the universal designation UNS N06022. It is a nickel-chromium-molybdenum solid solution strengthened super-alloy with a nominal chemical composition of 56% nickel， 22% chromium， and 13% molybdenum， with additions of iron， tungsten， and cobalt.
Distinctive Characteristic
Oxidation Resistance
C22 has excellent resistance to oxidation， carburization， and sulfidation at elevated temperatures. However， C22 should not be used at temperatures above 1250°F.
Corrosion Resistance
Alloy C22 is one of the most corrosion-resistant alloys available， even outperforming C276 and 625. It is resistant to almost all reducing and oxidizing environments， including strong oxidizers， seawater， and organic acids. In addition， C22 has excellent resistance to chloride-induced localized corrosion， including pitting， crevice corrosion， and stress corrosion cracking.
Chemical Composition % max Low C Ni-Cr-Mo
| Ni | Cr | Mo | Fe | W | C | Si | Co | Mn | V | P | S |
| remainderA | 20-22.5 | 12.5-14.5 | 2-6 | 2.5-3.5 | 0.015 | 0.08 | 2.5 | 0.5 | 0.35 | 0.02 | 0.02 |
(A) The composition of the remainder element shall be determined by arithmetic difference.
Mechanical Property
| Alloy | Density | Tensile Strength min | Yield Strength min | Elongation |
| UNS NO6022 | 8.69 g/cm3 | 100ksi，690MPa | 45ksi，310MPa | 45% |
C22 can be cold worked to higher strength levels. And it is typically annealed at 2050°F (1121°C)， followed by rapid cooling.
Applications
Chemical Processing
Food Processing
Pharmaceutical Industry
Oil & Gas
Power Generation
Pulp & Paper Industries