| Type: | Seamless | Standard: | ASTM A213/ASME SA213 |
|---|---|---|---|
| Material: | TP321/S32100/1.4541 | Finish: | Bright Annealing |
| Length: | 6M Or Specified Length As Required | Packing: | Ply Wooden Case |
| High Light: | Bright Annealed Stainless Steel Tube TP321， Stainless Steel Bright Annealed Pipe， ASME SA213 Bright Steel Tube | ||
ASTM A213/ASME SA213 TP321/S32100/1.4541 STAINLESS STEEL BRIGHT ANNEALED TUBE
Overview:
ASTM A312 TP 321/321H Tubes is titanium stabilize austenitic stainless steel with good quality specific corrosion resistance. It has exceptional resistance to intergranular oxidization after exposure to temperatures in the chromium carbide rainfall range of 800-1500°F (427-816°C). The alloy resists decay to 1500°F (816°C) and has elevated creep and stress break properties than alloys 304 and 304H. It also possesses good low-temperature toughness. It cannot be toughened by heat treatment， only by cold working. It can be without difficulty welded and processed by standard shop fabrication practices.
It exhibits high-quality general corrosion opposition that is comparable to 304. It was industrial for use in the chromium carbide rainfall range of 1800-1500°F (427-816°C) somewhere un-stabilized alloys such as 304 are subject to intergranular attack. The alloy can be used to having to dilute organic acids at restrained temperatures and in pure phosphoric acid at lesser temperatures and up to 10% weak solutions at elevated temperatures. Ganpat Industrial Corporation used different types of tubes in shapes it was manufacture in national and international.
Specification:
| Specification | ASTM A-213 & Its equivalent ASME， DIN & EN Standard. |
| Grades | 321， 321H |
| Type | Seamless Ferritic and Austenitic Boiler， Superheater， and Heat-Exchanger Tubes |
| Outer Diameter Size | 1/4” OD， NB to 6” OD， NB sizes |
| Thickness | 0.41mm to 25.4mm |
| Length | Up to 6 meters， custom cut lengths |
| Ends | No.1 Pickled Finish， No.4 finish， BA Finish， Electropolished Seamless Tubes |
| Delivery Conditions | As Rolled， Formed， Stress Relieved， Annealed， Hardened， Tempered， Cold Draw |
| Other Testing | Product Analysis， Transverse Tension Test， Flattening Test， Etching Test， Radiographic Examination， Stabilizing Heat Treatment， Intergranular Corrosion Test， Weld Decay Test， Magnetic Particle Detection， Grain Size Test， NACE 0175， Dual Grade， PWHT (POST WELD HEAT TREATMENT)， Flare Test， Bend Test， Hardness Test， Tensile Test etc |
| Dimension | All Pipes & Tube Is Manufactured and Inspected / Tested to the Relevant standards including ASTM and ASME |
| Packaging | Loose / Bundle / Wooden Pallet / Wooden Box / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
Chemical Composition:
| Grade | UNS | C | Mn | P | S | Si | Cr | Ni | Ti |
| 321 | S32100 | 0.08 max | 2.00 max | 0.045 max | 0.03 max | 1.00 max | 17.0-19.0 | 9.0-12.0 | 5(C+N)-0.07 |
| 321H | S32109 | 0.04-0.10 | 2.00 max | 0.045 max | 0.03 max | 1.00 max | 17.0-19.0 | 9.0-12.0 | 4(C+N)-0.07 |
Mechanical Properties:
| Grade | Tensile Strength， min， ksi (MPa) | Yield Strength， min， ksi (MPa) | Elongation in 2 in. or 50mm， min (%) | Hardness | Solutioning Temperature， min， °F(°C) | |
| Rockwell | Brinell/Vickers | |||||
| 321 | 75(515) | 30(205) | 35 | 90HRB | 192HBW/200HV | 1900(1040) |
| 321H | 75(515) | 30(205) | 35 | 90HRB | 192HBW/200HV | 2000(1090) |
Equivalent Grades:
| Standard | WERKSTOFF NR. | Unified Numbering System | European Standards | AFNOR | British Standards | GOST | Japanese Standards |
| 321 | 1.4541 | S32100 | X6CrNiTi18-10 | – | 321S31 | 08KH18N10T | SUS 321 |
| 321H | 1.4878 | S32109 | X8CrNiTi18-10 | – | 321S51 | 12KH18N10T | SUS 321H |
Applications:
1.Food preparation equipment particularly in chloride environments.
2.Laboratory benches & equipment.
3.Coastal architectural panelling， railings & trim.
4.Boat fittings.
5.Chemical containers， including for transport.
6.Heat Exchangers.
7.Woven or welded screens for mining， quarrying & water filtration.
8.Threaded fasteners.
9.Springs.