| AISI 1035 Steel, cold drawn, 19-32 mm (0.75-1.25 in) round | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelMedium Carbon Steel |
| Material Notes: | Water-hardening steels suitable for small parts of moderate strength. Used in levers, bolts, nuts, studs, and similar parts which are headed, upset, or extruded. |
| Key Words: | UNS G10350, AMS 5080, AMS 5082, ASTM A29, ASTM A108, ASTM A510, ASTM A519, carbon steels |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.85 g/cc | 0.284 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 163 | 163 | |
| Hardness, Knoop | 184 | 184 | Converted from Brinell |
| Hardness, Rockwell B | 84 | 84 | Converted from Brinell |
| Hardness, Vickers | 170 | 170 | Converted from Brinell |
| Tensile Strength, Ultimate | 550 MPa | 79800 psi | |
| Tensile Strength, Yield | 460 MPa | 66700 psi | |
| Elongation at Break | 12 % | 12 % | In 50 mm |
| Reduction of Area | 35 % | 35 % | |
| Modulus of Elasticity | 196 GPa | 28400 ksi | |
| Bulk Modulus | 156 GPa | 22600 ksi | Estimated from elastic modulus |
| Poissons Ratio | 0.29 | 0.29 | Typical for steel |
| Machinability | 65 % | 65 % | Based on AISI 1212 steel = 100% |
| Shear Modulus | 76.0 GPa | 11000 ksi | Estimated from elastic modulus |
| Electrical Properties | Metric | English | Comments |
Electrical Resistivity  | 0.0000163 ohm-cm @Temperature 0.000 °C | 0.0000163 ohm-cm @Temperature 32.0 °F | annealed specimen |
| 0.0000217 ohm-cm @Temperature 100 °C | 0.0000217 ohm-cm @Temperature 212 °F | annealed specimen | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 – 100 °C | 6.11 µin/in-°F @Temperature 68.0 – 212 °F | |
| 12.6 µm/m-°C @Temperature 0.000 – 300 °C | 7.00 µin/in-°F @Temperature 32.0 – 572 °F | ||
| 13.9 µm/m-°C @Temperature 0.000 – 500 °C | 7.72 µin/in-°F @Temperature 32.0 – 932 °F | ||
| Specific Heat Capacity | 0.486 J/g-°C @Temperature >=100 °C | 0.116 BTU/lb-°F @Temperature >=212 °F | annealed |
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.31 – 0.38 % | 0.31 – 0.38 % | |
| Iron, Fe | 98.63 – 99.09 % | 98.63 – 99.09 % | As remainder |
| Manganese, Mn | 0.60 – 0.90 % | 0.60 – 0.90 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.