| AISI 1022 Steel, as rolled | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelLow Carbon Steel |
| Material Notes: | Has fair machinability, fair to good weldability, and excellent formability. Cold drawing markedly increases the tensile strength of 1022 steel. |
| Key Words: | UNS G10220 |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.858 g/cc | 0.2839 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 149 | 149 | |
| Hardness, Knoop | 169 | 169 | Converted from Brinell |
| Hardness, Rockwell B | 80 | 80 | Converted from Brinell |
| Hardness, Vickers | 155 | 155 | Converted from Brinell |
| Tensile Strength, Ultimate | 505 MPa | 73200 psi | |
| Tensile Strength, Yield | 360 MPa | 52200 psi | |
| Elongation at Break | 35 % | 35 % | In 50 mm |
| Reduction of Area | 67 % | 67 % | |
| Modulus of Elasticity | 205 GPa | 29700 ksi | Typical for steel |
| Bulk Modulus | 160 GPa | 23200 ksi | Typical for steel |
| Poissons Ratio | 0.29 | 0.29 | Typical For Steel |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Izod Impact | 81.0 J | 59.7 ft-lb | |
| Electrical Properties | Metric | English | Comments |
Electrical Resistivity  | 0.0000159 ohm-cm @Temperature 0.000 °C | 0.0000159 ohm-cm @Temperature 32.0 °F | annealed specimen |
| 0.0000219 ohm-cm @Temperature 100 °C | 0.0000219 ohm-cm @Temperature 212 °F | annealed specimen | |
| 0.0000293 ohm-cm @Temperature 200 °C | 0.0000293 ohm-cm @Temperature 392 °F | annealed specimen | |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 0.472 J/g-°C | 0.113 BTU/lb-°F | Typical steel |
| Thermal Conductivity | 49.8 W/m-K | 346 BTU-in/hr-ft²-°F | Typical steel |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.17 – 0.23 % | 0.17 – 0.23 % | |
| Iron, Fe | 98.68 – 99.13 % | 98.68 – 99.13 % | As remainder |
| Manganese, Mn | 0.70 – 1.0 % | 0.70 – 1.0 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
Click here to view
all the property values for this datasheet as they were originally entered into MatWeb.