| AISI 1017 Steel, hot rolled, 19-32 mm (0.75-1.25 in) round | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelLow Carbon Steel |
| Material Notes: | Supplied as killed, semikilled, rimmed, and capped steel. Good weldability, relatively soft and strengthen with cold work during forming or drawing. Widely used in cold forming operations such as heading, upsetting, and extrusion. Used in the as-rolled condition as bar, shapes, sheet, and strip. |
| Key Words: | UNS G10170, ASTM A29, ASTM A108, ASTM A510, ASTM A513, ASTM A519, ASTM A544, ASTM A549, ASTM A575, ASTM A576, ASTM A659, MIL SPEC MIL-S-11410 (CS1017), SAE J403, JIS S 17 C, JIS S 15 CK, SS14 1370 (Sweden), SAE J412, SAE J414, DIN 1.1141, AFNOR XC 15 (Fr), AFNOR XC 18 (Fr), JIS S 15 C, AISI1017 |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Typical for steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 105 | 105 | |
| Hardness, Knoop | 123 | 123 | Converted from Brinell |
| Hardness, Rockwell B | 60 | 60 | Converted from Brinell |
| Hardness, Vickers | 108 | 108 | Converted from Brinell |
| Tensile Strength, Ultimate | 365 MPa | 52900 psi | |
| Tensile Strength, Yield | 200 MPa | 29000 psi | |
| Elongation at Break | 26 % | 26 % | in 50 mm |
| Reduction of Area | 50 % | 50 % | |
| Modulus of Elasticity | 200 GPa | 29000 ksi | Typical for steel |
| Bulk Modulus | 160 GPa | 23200 ksi | Typical for steel |
| Poissons Ratio | 0.29 | 0.29 | Typical For Steel |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000159 ohm-cm @Temperature 0.000 °C | 0.0000159 ohm-cm @Temperature 32.0 °F | estimated by comparison with similar materials |
| Thermal Properties | Metric | English | Comments |
CTE, linear  | 11.5 µm/m-°C @Temperature 20.0 °C | 6.39 µin/in-°F @Temperature 68.0 °F | Typical steel |
| 12.2 µm/m-°C @Temperature 0.000 – 300 °C | 6.78 µin/in-°F @Temperature 32.0 – 572 °F | Typical for steel | |
| 13.9 µm/m-°C @Temperature 0.000 – 500 °C | 7.72 µin/in-°F @Temperature 32.0 – 932 °F | Typical for steel | |
| Specific Heat Capacity | 0.481 J/g-°C @Temperature >=95.0 °C | 0.115 BTU/lb-°F @Temperature >=203 °F | condition unknown |
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | estimated based on similar materials |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.14 – 0.20 % | 0.14 – 0.20 % | |
| Iron, Fe | 99.11 – 99.56 % | 99.11 – 99.56 % | As remainder |
| Manganese, Mn | 0.30 – 0.60 % | 0.30 – 0.60 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
Click here to view
all the property values for this datasheet as they were originally entered into MatWeb.