| AISI 1015 Steel, mock carburized at 915°C (1680°F) for 8 hours, 775°C (1430°F) reheat, water quenched, 175°C (350°F) temper, 13 mm (0.5 in.) round | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelLow Carbon Steel |
| Material Notes: | Better machinability and carburizing. Can be strengthened by cold working or surface hardened by carburizing or cyaniding. Hot rolled sheet has excellent weldability. Post water quenched hardness: 36.5 HRC surface, 23 HRC half-radius, 22 HRC Center. |
| Key Words: | UNS G10150, AMS 5060, ASTM A29, ASTM A108, ASTM A510, ASTM A545, ASTM A549, ASTM A575, ASTM A576, ASTM A659, FED QQ-S-698 (C1015), MIL SPEC MIL-S-16974, SAE J403, JIS S 17 C, JIS S 15 CK, SS14 1370 (Sweden), SAE J412, SAE J414, DIN 1.1141, AFNOR XC 15 (Fr), AFNOR XC 18 (Fr), JIS S 15 C, AISI1015 |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Typical for steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 217 | 217 | |
| Hardness, Knoop | 240 | 240 | Converted from Brinell |
| Hardness, Rockwell B | 95 | 95 | Converted from Brinell |
| Hardness, Rockwell C | 17 | 17 | Converted from Brinell hardness. Below normal Rockwell C hardness range, for comparison only. |
| Hardness, Vickers | 228 | 228 | Converted from Brinell |
| Tensile Strength, Ultimate | 733 MPa | 106000 psi | |
| Tensile Strength, Yield | 415 MPa | 60200 psi | |
| Elongation at Break | 15 % | 15 % | in 50 mm |
| Reduction of Area | 32.9 % | 32.9 % | |
| Modulus of Elasticity | 200 GPa | 29000 ksi | Typical for steel |
| Bulk Modulus | 160 GPa | 23200 ksi | Typical for steel |
| Poissons Ratio | 0.29 | 0.29 | Typical For Steel |
| Machinability | 60 % | 60 % | Based on 100% machinability for AISI 1212 steel. |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
Electrical Resistivity  | 0.0000159 ohm-cm @Temperature 0.000 °C | 0.0000159 ohm-cm @Temperature 32.0 °F | annealed condition |
| 0.0000219 ohm-cm @Temperature 100 °C | 0.0000219 ohm-cm @Temperature 212 °F | annealed condition | |
| 0.0000292 ohm-cm @Temperature 200 °C | 0.0000292 ohm-cm @Temperature 392 °F | annealed condition | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.9 µm/m-°C @Temperature 0.000 – 100 °C | 6.61 µin/in-°F @Temperature 32.0 – 212 °F | |
| 12.4 µm/m-°C @Temperature 0.000 – 200 °C | 6.89 µin/in-°F @Temperature 32.0 – 392 °F | ||
| 13.0 µm/m-°C @Temperature 0.000 – 300 °C | 7.22 µin/in-°F @Temperature 32.0 – 572 °F | ||
| 13.5 µm/m-°C @Temperature 0.000 – 400 °C | 7.50 µin/in-°F @Temperature 32.0 – 752 °F | ||
| 14.2 µm/m-°C @Temperature 0.000 – 500 °C | 7.89 µin/in-°F @Temperature 32.0 – 932 °F | ||
| Specific Heat Capacity | 0.486 J/g-°C @Temperature >=100 °C | 0.116 BTU/lb-°F @Temperature >=212 °F | annealed |
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | estimated based on similar materials |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.13 – 0.18 % | 0.13 – 0.18 % | |
| Iron, Fe | 99.13 – 99.57 % | 99.13 – 99.57 % | As remainder |
| Manganese, Mn | 0.30 – 0.60 % | 0.30 – 0.60 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
Click here to view
all the property values for this datasheet as they were originally entered into MatWeb.