| AISI 1012 Steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round or thickness | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelLow Carbon Steel |
| Material Notes: | 16017b3906a94e2c9fd52bb7a0833749Easily cold formed by heading, extruding, upsetting, bending, and other deforming processes. Uses for wires include electroplated products, such as racks, storage bins, shopping carts, fan guards, and jewelry, and unplated such as wires, staples, hardware, and barbed wire. |
| Key Words: | UNS G10120, AISI1012, ASTM A29, ASTM A510, ASTM A519, ASTM A545, ASTM A549, ASTM A575, ASTM A576, MIL SPEC MIL-S-11310 (CS1012), SAE J403, SAE J412, SAE J414 |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Typical for steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 95 | 95 | |
| Hardness, Knoop | 113 | 113 | Converted from Brinell |
| Hardness, Rockwell B | 55 | 55 | Converted from Brinell |
| Hardness, Vickers | 98 | 98 | Converted from Brinell |
| Tensile Strength, Ultimate | 330 MPa | 47900 psi | |
| Tensile Strength, Yield | 185 MPa | 26800 psi | |
| Elongation at Break | 28 % | 28 % | in 50 mm |
| Reduction of Area | 50 % | 50 % | |
| Modulus of Elasticity | 200 GPa | 29000 ksi | Typical for steel |
| Bulk Modulus | 160 GPa | 23200 ksi | Typical for steel |
| Poissons Ratio | 0.29 | 0.29 | Typical For Steel |
| Machinability | 55 % | 55 % | Based on AISI 1212 steel = 100%. Group I bar, rod, and wire products machinability can be improved by cold drawing. |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000174 ohm-cm | 0.0000174 ohm-cm | Typical steel |
| Thermal Properties | Metric | English | Comments |
CTE, linear  | 11.5 µm/m-°C @Temperature 20.0 °C | 6.39 µin/in-°F @Temperature 68.0 °F | Typical steel |
| 12.2 µm/m-°C @Temperature 0.000 – 300 °C | 6.78 µin/in-°F @Temperature 32.0 – 572 °F | Typical for steel | |
| 13.9 µm/m-°C @Temperature 0.000 – 500 °C | 7.72 µin/in-°F @Temperature 32.0 – 932 °F | Typical for steel | |
| Specific Heat Capacity | 0.472 J/g-°C | 0.113 BTU/lb-°F | Typical steel |
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | Typical steel |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.10 – 0.15 % | 0.10 – 0.15 % | |
| Iron, Fe | 99.16 – 99.6 % | 99.16 – 99.6 % | As remainder |
| Manganese, Mn | 0.30 – 0.60 % | 0.30 – 0.60 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding