| AISI 1064 Steel, hot rolled, 19-32 mm (0.75-1.25 in) round | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelHigh Carbon Steel |
| Material Notes: | Applications include springs for upholstered furniture and automotive seats and backs. |
| Key Words: | UNS G10640, ASTM A26, ASTM A29, ASTM A57, ASTM A230, ASTM A682, SAE J403, SAE J412, SAE J414, DIN 1.221, AFNOR XC 60 (Fr), AFNOR XC 65 (Fr), SS14 1665 (Sweden), SS14 1678 (Sweden) |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Typical for steel. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 201 | 201 | |
| Hardness, Knoop | 223 | 223 | Converted from Brinell |
| Hardness, Rockwell B | 93 | 93 | Converted from Brinell |
| Hardness, Rockwell C | 13 | 13 | Converted from Brinell hardness. Value below normal HRC range, for comparison purposes only. |
| Hardness, Vickers | 211 | 211 | Converted from Brinell |
| Tensile Strength, Ultimate | 670 MPa | 97200 psi | |
| Tensile Strength, Yield | 370 MPa | 53700 psi | |
| Elongation at Break | 12 % | 12 % | in 50 mm |
| Reduction of Area | 30 % | 30 % | |
| Modulus of Elasticity | 200 GPa | 29000 ksi | Typical for steel |
| Bulk Modulus | 160 GPa | 23200 ksi | Typical for steel |
| Poissons Ratio | 0.29 | 0.29 | Typical For Steel |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000174 ohm-cm | 0.0000174 ohm-cm | Typical steel |
| Thermal Properties | Metric | English | Comments |
CTE, linear  | 11.6 µm/m-°C @Temperature 0.000 – 100 °C | 6.44 µin/in-°F @Temperature 32.0 – 212 °F | |
| 12.6 µm/m-°C @Temperature 0.000 – 200 °C | 7.00 µin/in-°F @Temperature 32.0 – 392 °F | ||
| 13.3 µm/m-°C @Temperature 0.000 – 300 °C | 7.39 µin/in-°F @Temperature 32.0 – 572 °F | ||
| 14.0 µm/m-°C @Temperature 0.000 – 400 °C | 7.78 µin/in-°F @Temperature 32.0 – 752 °F | ||
| Specific Heat Capacity | 0.472 J/g-°C | 0.113 BTU/lb-°F | Typical steel |
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | Typical steel |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.60 – 0.70 % | 0.60 – 0.70 % | |
| Iron, Fe | 98.41 – 98.9 % | 98.41 – 98.9 % | As remainder |
| Manganese, Mn | 0.50 – 0.80 % | 0.50 – 0.80 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.