| AISI 1019 Steel, cold drawn | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelLow Carbon Steel |
| Material Notes: | Medium low-carbon steel has good weldability and slightly better machinability than lower carbon steels. |
| Key Words: | SAE J403, SAE J412, SAE J414, SAE J1397, FED QQ-S-633, MIL R-6532, MIL R-908, MIL-S-12505, MIL-S- 16113, MIL-S-20166, UNS G10190, ASTM A29, ASTM A510, ASTM A513, ASTM A519, ASTM A545, ASTM A548, ASTM A576, ASTM A635, ASTM A830 |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 131 | 131 | |
| Hardness, Knoop | 150 | 150 | Converted from Brinell |
| Hardness, Rockwell B | 73 | 73 | Converted from Brinell |
| Hardness, Vickers | 136 | 136 | Converted from Brinell |
| Tensile Strength, Ultimate | 455 MPa | 66000 psi | |
| Tensile Strength, Yield | 379 MPa | 55000 psi | |
| Elongation at Break | 15 % | 15 % | In 50 mm |
| Reduction of Area | 40 % | 40 % | |
| Modulus of Elasticity | 205 GPa | 29700 ksi | Typical for steel |
| Bulk Modulus | 160 GPa | 23200 ksi | Typical for steel |
| Poissons Ratio | 0.29 | 0.29 | Typical For Steel |
| Machinability | 70 % | 70 % | Based on AISI 1212 steel = 100% |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000159 ohm-cm @Temperature 0.000 °C | 0.0000159 ohm-cm @Temperature 32.0 °F | estimated by comparison with similar steel alloys |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 0.472 J/g-°C | 0.113 BTU/lb-°F | Typical steel |
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | Typical steel |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.14 – 0.20 % | 0.14 – 0.20 % | |
| Iron, Fe | 98.71 – 99.16 % | 98.71 – 99.16 % | As remainder |
| Manganese, Mn | 0.70 – 1.0 % | 0.70 – 1.0 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
Click here to view
all the property values for this datasheet as they were originally entered into MatWeb.