| AISI 1006 Steel, cold drawn | |
|---|---|
| Categories: | MetalFerrous MetalCarbon SteelAISI 1000 Series SteelLow Carbon Steel |
| Material Notes: | The composition listed is for standard grade for wire and rod. Applications: Soft, very ductile, used in applications which require severe bending and welding such as panels for automobiles or appliances. Also used in magnet core applications. |
| Key Words: | UNS G10060, ASME 5041, ASTM A29, ASTM A510, ASTM A545, FED QQ-W-461, MIL SPEC MIL-S-11310 (CS1006), SAE J403, SAE J412, SAE J414, AISI1006 |
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
 Printer friendly version Download to Excel (requires Excel and Windows)
Add to Folder: | |
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.872 g/cc | 0.2844 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 95 | 95 | |
| Hardness, Knoop | 113 | 113 | Converted from Brinell |
| Hardness, Rockwell B | 55 | 55 | Converted from Brinell |
| Hardness, Vickers | 98 | 98 | Converted from Brinell |
| Tensile Strength, Ultimate | 330 MPa | 47900 psi | |
| Tensile Strength, Yield | 285 MPa | 41300 psi | |
| Elongation at Break | 20 % | 20 % | In 50 mm |
| Reduction of Area | 45 % | 45 % | |
| Modulus of Elasticity | 206 GPa | 29900 ksi | |
| Bulk Modulus | 163 GPa | 23600 ksi | Estimated from elastic modulus |
| Poissons Ratio | 0.29 | 0.29 | Typical for steel |
| Machinability | 50 % | 50 % | Based on AISI 1212 steel = 100%. Group I bar, rod, and wire products machinability can be improved by cold drawing. |
| Shear Modulus | 80.0 GPa | 11600 ksi | Estimated from elastic modulus |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000174 ohm-cm | 0.0000174 ohm-cm | Typical steel |
| Thermal Properties | Metric | English | Comments |
CTE, linear  | 12.6 µm/m-°C @Temperature 0.000 – 100 °C | 7.00 µin/in-°F @Temperature 32.0 – 212 °F | |
| 13.5 µm/m-°C @Temperature 0.000 – 300 °C | 7.50 µin/in-°F @Temperature 32.0 – 572 °F | ||
| 13.7 µm/m-°C @Temperature 0.000 – 1000 °C | 7.61 µin/in-°F @Temperature 32.0 – 1830 °F | ||
| 14.2 µm/m-°C @Temperature 0.000 – 500 °C | 7.89 µin/in-°F @Temperature 32.0 – 932 °F | ||
| Specific Heat Capacity | 0.481 J/g-°C | 0.115 BTU/lb-°F | 50-100ºC |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | <= 0.080 % | <= 0.080 % | |
| Iron, Fe | 99.43 – 99.75 % | 99.43 – 99.75 % | As remainder |
| Manganese, Mn | 0.25 – 0.40 % | 0.25 – 0.40 % | |
| Phosphorus, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units.
We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb’s terms of use regarding this information.
Click here to view
all the property values for this datasheet as they were originally entered into MatWeb.