| Material Grade: | TP304L | Standard: | ASTM A213 |
|---|---|---|---|
| Size: | 6 ā 530mm | W.T.: | 0.50 ā 64mm |
| Length: | 1000mm-12500mm | NDT: | ET HT UT PT |
| Packing: | Ply-wooden Case /Iron Case/ Bundle | Appllication: | Heat Exchanger/ Chemical |
| High Light: | TP304L Stainless Steel Round Tubeļ¼ Chemical Stainless Steel Seamless Tubesļ¼ Heat Exchangers Seamless Stainless Steel Pipe | ||
ASTM A213 TP304L Stainless Steel Seamless Tubes For Heat Exchangers Chemical
ASTM A213 A312 A269 A511 A240 UNS S30403 304Lļ¼ EN 10216-5 1.4307 stainless steel tubing is a variant of the 18% chromium – 8% nickel austenitic alloy that is the most familiar and frequently used alloy in the stainless steel family. This alloy can be considered for a wide range of applications and exhibits good corrosion resistanceļ¼ ease of fabricationļ¼ excellent malleabilityļ¼ high strength with low weight. type 304L is a lower carbon variant of grade 304 – the steel can be welded without causing problems with carbon precipitation of chromium carbideļ¼ as the steel is depleted of chromium during the welding processļ¼ thus reducing its effectiveness against corrosion/oxidationļ¼ and due to the low carbon percentage. intergranular corrosion attack can be minimized.
Thereforeļ¼ Type 304L is a sort after material for use in severe corrosive conditions. Welding annealing is only necessary if the stress load is excessive in the application. This steel grade is found in various commercial sectorsļ¼ especially in the chemical industry. 304 and 304L have similar properties and in some cases are stocked with dual certificationļ¼ it is concluded that the properties and composition of each item conform to both types of steel. 304H grade cannot be included in this equation because of the higher carbon content of the steelļ¼ intended for high temperature applications.
Chemical Composition of ASTM A213 TP304L Stainless Steel Seamless Tubes
| Grade | – | C | Mn | Si | P | S | Cr | Mo | Ni | N |
| 304L/S30403 | min.max. | -0.035 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | – | 8.0-12.0 | – |
| 304/S30400 | min.max. | -0.08 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | – | 8.0-11.0 | – |
| EN 10216-5 1.4301 | min.max. | -0.07 | -2 | -1 | -0.04 | -0.015 | 17.00-19.5 | – | 8.0-10.5 | -0.11 |
| EN 10216-5 1.4307 | min.max. | -0.03 | -2 | -1 | -0.04 | -0.015 | 17.5-19.5 | – | 8.0-10.0 | -0.11 |
| 304H /S30409 | min.max. | 0.04-0.10 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | – | 8.0-11.0 | – |
| EN 10216-5 1.4948 | min.max. | 0.04-0.08 | -2 | -1 | -0.035 | -0.015 | 17.0-19.0 | – | 8.0-11.0 | -0.11 |
Mechanical Property of ASTM A213 TP304L Stainless Steel Seamless Tubes
| – | Tensile Strength | Yield Strength | Elongation | Hardness | Hardness |
| Grade | (MPa) min | 0.2% Proof (MPa) min | (% in 50mm) min | Rockwell B (HR B) max | Brinell (HB) max |
| 304 | 515 | 205 | 35 | 90 | 192 |
| 304L | 485 | 170 | 35 | 90 | 192 |
Physical Properties Of ASTM A213 TP304L Stainless Steel Seamless Tubes
| 304L Stainless Steel Pipe Density (lb / cu. in.) | 0.29 |
| Specific Gravity(kgs/dm³) | 7.93 |
| Specific Heat (Btu/lb/Deg°F – [32-212 Deg °F]) | 0.12 |
| Electrical Resistivity (microhm-cm (at 68 Deg °F)) | 432 |
| Melting Point (Deg°F) | 2650 |
| Modulus of Elasticity Tension | 28 |