| Specification: | ASTM A269. ASME SA269， EN10216-5 ， GOST9941-91， JIS 3459， DIN17458 | Grade: | TP316Ti， (UNS S31635) |
|---|---|---|---|
| Type: | Seamless， Welded， U-bend | Surface: | Pickled And Annealed， Polished， Bright Annealed |
| Non Destructive Test: | Eddy Current Test -ASTM E426， Hystostatic Test-ASTM A999， Ultrsonic Test -ASTM E213 | Size Standard: | ASTM B16.10 & B16.19 & Customized |
| High Light: | Stainless Steel Seamless Tube TP316Ti， Seamless Ss Tube 2500mm， Stainless Seamless Steel Pipe | ||
ASTM A269 TP316Ti UNS S31635 Seamless Tube Chemical Containers
TP316Ti (UNS S31635) is a titanium stable version of 316 molybdenum austenitic stainless steel. 316 alloy is more resistant to general and pitting/gap corrosion than traditional chrome-nickel austenitic stainless steel (e.g. 304). They also provide higher creep， stress fracture and tensile strength at high temperatures.
ASTM A269 TP316Ti Stainless Steel Tubes
Stainless steel is often called corrosion-resistant steel — it doesn't stain， corrode， or rust as easily as normal carbon steel. However， it is misleading to say that it is corrosion resistant. It differs significantly from standard carbon steel due to its chromium content， which limits surface corrosion， and carbon steel rusts when exposed to any moisture in the air and atmosphere. Stainless steel is often a popular solution due to its oxidation resistance properties.
Chemical Composition
Element | Min | Max |
C | – | 0.08 |
Si | – | 0.75 |
Mn | – | 2 |
P | – | 0.45 |
S | – | 0.03 |
Cr | 16 | 18 |
Mo | 2 | 3 |
N | – | 0.1 |
Fe | Balance | |
Ni | 10 | 14 |
Ti | 5x%(C+N) | |
Equivalent Material
| STANDARD | WERKSTOFF NR. | UNS | GOST | AFNOR | BS | JIS | EN |
| SS 316TI | 1.4571 | S31635 | 08Ch17N13M2T | Z6CNDT17‐12 | 320S31 | SUS 316Ti | X6CrNiMoTi17-12-2 |
Mechanical Properties
Temper | Annealed | |
|---|---|---|
Tensile Rm | 75 | ksi (min) |
Tensile Rm | 515 | MPa (min) |
R.p. 0.2% Yield | 30 | ksi (min) |
R.p. 0.2% Yield | 205 | MPa (min) |
Elongation (2” or 4D gl) | 35 | % (min) |
ASTM A269 316Ti Tube Tolerances
Size | Tolerances， Inches | |||
OD， | Wall | Ovality | Cut Length | |
Less than 1/2 | ±0.005 | ±15% | —— | +1/8 |
Over 1/2 to 1-1/2 | ±0.005 | ±10% | –0.065 | |
Over 1-1/2 to 3-1/2 | ±0.010 | ±10% | –0.095 | +3/16 |
Over 3-1/2 to 5-1/2 | ±0.015 | ±10% | –0.150 | |
Over 5-1/2 to 8 | ±0.030 | ±10% | ——
| |
Physical Properties
Specific Heat (0-100°C) | 500 | J.kg-1.°K-1 |
Thermal Conductivity | 14.6 | W.m -1.°K-1 |
Thermal Expansion | 16.5 | mm/m/°C |
Modulus Elasticity | 193 | GPa |
Electrical Resistivity | 7.4 | μohm/cm |
Density | 7.99 | g/cm3 |
Applications
-Military products
-Semiconductors
-Biomedicine
-Precision instruments
-Hydraulic parts
-Other industrial products